ZR230C
Parslen ZR230C is a high molecular weight Random Polypropylene Copolymer for compression molding and extrusion. Parslen ZR230C exhibits excellent heat resistance, and is designed to produce items with superior toughness, even at low temperature. Because of its excellent impact strength and its improved creep rupture properties under internal pressure stress, Parslen ZR230C is well suited for production of pressure pipes for industry, heating pipes and under floor hot water heating, domestic service pipes (hot and cold water) and wieldable fittings.
Data Sheet
Typical Properties [a,b] | Method | Unit | Value (a) | Tolerance |
Melt Flow Rate(230 ℃, 2.16 Kg) | ASTM D 1238 | gr/10 min | 0.35 | ±0.5 |
Melt Flow Rate (230 ℃, 5.0 Kg) | ASTM D 1238 | gr/10 min | 1.7 | ±0.2 |
Vicat Softening Point (9.8 N) | ASTM D 1525 | ℃ | 135 | ±5 |
H.D.T. (0.46 MPa) | ASTM D 648 | ℃ | 75 | ±8 |
Flexural Modulus | ASTM D 790 | MPa | 1000 | ± 120 |
Tensile Strength at Yield | ASTM D 638 | MPa | 28 | ±4 |
Elongation at Yield | ASTM D 638 | % | 15 | -2 |
Izod Impact Strength (Notched) at 23°C |
ASTM D 256 | J/m | No Break | – |
Izod Impact Strength (Notched) at -20° C |
ASTM D 256 | J/m | 50 | ±5 |
Rockwell Hardness (R – B Scale) | ASTM D 785 | R-B | 75 | + 10 |
a) Values shown are averages and are not to be considered as exact product specifications.
b) All specimens are prepared by injection molding. (Last revised 10. Aug 2011).
Packaging
750 Kg Jumbo Bags
1375 Kg Bags per pallet (55*25kg bags)
Transportation
- Rail
- Land
- Sea
Application
Extrusion applications of Parslen ZR230C include:
- Profiles
- Pipes and tough sheet for industrial applications
This grade is especially suitable for applications requiring high resistance to temperature, pressure and aggressive media.