PBR 1220
High-Cis Polybutadiene rubber “1220” is produced by a technology of solution polymerization based on Ziegler-Natta (Cobalt) catalyst. It has more than 96% of 1.4 Cis content and very low glass transition temperature.
Cured “1220” has excellent properties such as abrasion resistance, tear strength, resilience, weathering resistance and low rolling resistance (good fuel economy) due to its low glass transtion temperature (Tg typically <-90 °C).
Data Sheet
| Typical Properties | Units | Values | Test Method |
| Mooney Viscosity (ML 1+4@100°C) | MU | 41-49 | ASTM D1646 |
| Cis Content | wt% | Min 96 | Internal Method |
| Volatile Material | wt% | Max 0.75 | ASTM D1416 |
| Ash Content | wt% | Max 0.3 | ASTM D1416 |
| Compound Mooney Viscosity | MU | Max 77 | ASTM D1646 |
| Tensile Strength (35 Min) | Kgf/cm 3 | Min 150 | ASTM D412 |
| Elongation at Break (35 Min) | % | Min 440 | ASTM D412 |
|
300% Modulus at 145°C |
|||
| 25 Min | Kgf/cm 3 | 68-108 | ASTM D412 |
| 35 Min | Kgf/cm 3 | 74-114 | ASTM D412 |
| 50 Min | Kgf/cm 3 | 74-114 | ASTM D412 |
Packaging
- 35±0.5 Kg bales wrapped with polyethylene film
- 36 bales per crate (1260±18 Kg)
Transportation
- Rail
- Land
- Sea
Application
Appropriate for:
- Rubber compounds used in the production of tire
- Flooe coverings
- Footwear
- Children toys
- Rubber hose
- Belts
- Golf balls