LL0209KJ
LL0209KJ is linear low density polyethylene copolymer containing butene-1(C4) as co monomer. It is suitable for blending with conventional LDPE. This grade available in the form of granules. Film made from pure LL0209KJ has the following advantages over LDPE: better sealing, higher puncture resistance, greater drawdown ability, easy opening properties at 2 layer film and higher tensile strength. This grade has food contact approval.
Data Sheet
| Property | – | Unit | Test Method | Typical Value |
| Melt Flow Index (190◦C 2.16Kg) |
– | g/10min | ASTM D-1238 | 0.9 |
| Density | – | gr/cm 3 | ASTM D-1505 | 0.921 |
| VICAT Softening Point | – | °C | ASTM D-1525 | 105 |
|
Film** |
||||
| Dart Drop Impact | Method A | GR | ASTM D-1709 | 140 |
| Tensile Stress at Yield | MD/TD | MPA | ASTM D-882 | 10/11 |
| Tensile Stress at Break | MD/TD | MPA | ASTM D-882 | 41/32 |
| Elongation at Break | MD/TD | % | ASTM D-882 | 620/840 |
| Haze | – | % | ASTM D-1003 | 12 |
| Gloss (45°) | – | %° | ASTM D-2457 | 56 |
*All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications)
**38µm film, 2.5:1 blow up ratio, 225°c melt temperature MD: Machine Direction, TD: Transverse Direction Grade Suffix (Additives Indication) KJ: GENERAL ANTIOXIDANT WITH SLIP AGENT / ANTIBLOCKING AGENTS
Packaging
1375 Kg Bag per pallet (55*25kg bags)
Transportation
- Rail
- Land
- Sea
Applications
- Green house film
- Silage film
- Hand bags
- General purpose film applications