LFI2130

LFI2130 is a high molecular weight, low density polyethylene for producing heavy-duty packaging films for applications like shrink hoods. It appears as pellet form. It contains no slip agent, antiblock but it contains antioxidant. It gives outstanding strength and toughness, draw down ability and very good biaxial shrink properties. LFI2130 has been manufactured under SABTEC licensed technology.

Data Sheet

Typical Properties Typical Value 1 Unit Test Method

Physical
MFI (190 °C /2.16 Kg ) 0.3 dg/min ISO 1133
Density 2 921 kg/m 3 ISO 1183 (A)

Mechanical 3

Impact Strength 31 kJ/m ASTM D4272
Tear Strength (TD) 45 kN/m ISO 6383-2
Tear Strength (MD) 20 kN/m ISO 6383-2
Yield Stress (TD) 10 MPa ISO 527-1,3
Yield Stress (MD) 11 MPa ISO 527-1,3
Tensile Stress at Break (TD) 24 MPa ISO 527-1,3
Tensile Stress at Break (MD) 22 MPa ISO 527-1,3
Strain at Break (TD) > 500 % ISO 527-1,3
Strain at Break (MD) > 350 % ISO 527-1,3
Modulus of Elasticity (TD) 150 MPa ISO 527-1,3
Modulus of Elasticity (MD) 140 MPa ISO 527-1,3
Coefficient of Friction 0.7 – ASTM D1894
Blocking < 5 g ASTM D3354
Re-blocking 20 g SABTEC method

Optical
Haze 12 % ASTM D1003 A
Gloss (45°) 55 GU ASTM D2457
Clarity 50 mV SABTEC method
Recommended Process Conditions 4
Extruder temperature profile: 185-210 °C Blow up ratio: 2-4
Film thickness: 45-150 μm.

1.Typical values: these are not to be construed as specifications.
2.The density parameter was determined on compression-molded specimens, which were prepared in accordance with procedure C of ASTM D4703, Annex A1.
3.Properties are based on 120 μm blown film produced at a melt temperature of 200°C and 3 BUR using 100% LFI2130.
4.Please note that, these processing conditions are recommended by producer only for 100% LFI2130 resin (not in the case of blending with any other compatible material), but because of the many particular factors which are outside our knowledge and control, and may affect the use of product, no warranty is given.

Packaging

25 Kg Bags

Transportation

  • Rail
  • Land
  • Sea

Application

  • Blown film extrusion
  • Heavy duty packaging film
  • Shrink hoods
  • Industrial sacks
  • Carrier bag and liners