Parslen ZH515MA is a Polypropylene homopolymer developed for the high speed extrusion of transparent cast and blown film. Parslen ZH515MA is formulated with an effective slip and antiblocking package and is suitable for the extrusion of low thickness films and can be used for films from 15 to 150 µm. In comparison with standard polypropylene types for film production, Parslen ZH515MA allows for faster processing due to its peculiar structure and composition. Films made with Parslen ZH515MA show a good behavior on the winding rolls and in the cutting section and feature a high transparency, a high gloss and a good printability after corona treatment.

Data Sheet

Typical Properties [a,b] Method Unit Value (a) Tolerance
Melt Flow Rate (230 ℃, 2.16 Kg) ASTM D 1238 gr/10 min 9 ±2
Vicat Softening point (9.8 N) ASTM D 1525 ℃ 151 ±5
H.D.T (0.46 MPa) ASTM D 648 ℃ 95 ±8
Flexural Modulus ASTM D 790 MPa 1200 ±120
Tensile Strength at Yield ASTM D 638 MPa 32 ±5
Elongation at Yield ASTM D 638 % 12 -2
Izod Impact Strength (Notched) at 23 ℃ ASTM D 256 J/m 37 ±4
Rockwell Hardness [R-B Scale] ASTM D 785 R – B 100 +20
Haze MTM 17031 % 2 ±0.5
Gloss MTM 17021 % 80 ±5

a) Values shown are averages and are not be considered as exact product specifications.
b) All specimens are prepared by injection molding. (Last revised 31, July 2008)

Packaging

750 Kg Jumbo Bags

1375 Kg Bags per pallet (55*25kg bags)

Transportation

  • Rail
  • Land
  • Sea

Application

  • Shopping bags and packaging for snacks
  • Bakery products
  • Books
  • Blankets
  • Hosiery and shirts
  • Stationery folders
  • Twines and ropes
  • Suitable for food contact
Menu